Uticaj mehaničke aktivacije na sistem MgO-Al2O3-SiO2 u prisustvu aditiva TeO2 / Influence of mechanical activation on MgO-Al2O3-SiO2 system in the presence of TeO2 additive
(Savez inženjera i tehničara Srbije, Beograd, 2016)
Ova istraživanja posvećena su uticaju mehaničke aktivacije na strukturu kordijeritne smeše 2MgO+2Al2O3+5SiO2. Praćena su i testirana dva paralelna sistema, jedan bez, i drugi u prisustvu 5 masenih % TeO2 kao aditiva. ...
Influence of prolonged sintering time on density and electrical properties of isothermally sintered cordierite-based ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2013)
Mehanička aktivacija je brza i jeftina procedura koja se obično koristi za pripremanje uzoraka pre procesa sinterovanja. Kordijerit, stehiometrijska mešavina tri različita oksida (2MgO⋅2Al2O3⋅5SiO2) je veoma atraktivan, i ...
Electrical properties of isothermally sintered cordierite-based ceramics as funcion of sintering and activation time
(Belgrade : Union of Mechanical and Electrotechnical Engineers and Technicians of Serbia (SMEITS)Belgrade : Society for Renewable Electrical Power Sources, 2021)
Mechanical activation is a commonly used and relatively fast and inexpensive procedure for
sample preparation before the sintering process. Cordierite is a stoichiometric mixture of three different
oxides (2MgO⋅2Al2O3⋅5SiO2). ...
The influence of high compaction pressure on cordierite-based ceramics
(Bor : University of Belgrade, Technical Faculty in Bor, 2021)
Cordierite, 2MgO⋅2Al2O3⋅5SiO2 is a high-temperature ceramic material. In order to improve its properties, titanium oxide was added to the starting mixture in an amount of 5%. Mechanical activation of samples was performed ...
SEM and X-ray analyses of sintered MgO/Bi2O3 binary system
(Bor : University of Belgrade, Technical Faculty in Bor, 2021)
Cordierite, 2MgO⋅2Al2O3⋅5SiO2 is a high-temperature ceramic material. In order to improve its properties, titanium oxide was added to the starting mixture in an amount of 5%. Mechanical activation of samples was performed ...