Uticaj mehaničke aktivacije na sistem MgO-Al2O3-SiO2 u prisustvu aditiva TeO2 / Influence of mechanical activation on MgO-Al2O3-SiO2 system in the presence of TeO2 additive
(Savez inženjera i tehničara Srbije, Beograd, 2016)
Ova istraživanja posvećena su uticaju mehaničke aktivacije na strukturu kordijeritne smeše 2MgO+2Al2O3+5SiO2. Praćena su i testirana dva paralelna sistema, jedan bez, i drugi u prisustvu 5 masenih % TeO2 kao aditiva. ...
Influence of prolonged sintering time on density and electrical properties of isothermally sintered cordierite-based ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2013)
Mehanička aktivacija je brza i jeftina procedura koja se obično koristi za pripremanje uzoraka pre procesa sinterovanja. Kordijerit, stehiometrijska mešavina tri različita oksida (2MgO⋅2Al2O3⋅5SiO2) je veoma atraktivan, i ...
Influence of sintering time on density properties and SEM analysis of cordierite-based ceramics
(Belgrade : Union of Mechanical and Electrotechnical Engineers and Technicians of Serbia (SMEITS) Society for Renewable Electrical Power SourcesBelgrade : Society for Renewable Electrical Power Sources, 2021)
The mechanical activation of the starting mixtures of cordierite (2MgO*2Al2O3*5SiO2) with
5.00 mass % TiO2 was performed in a high energy ball mill during 10-80 min. The applied compaction
pressure before the sintering ...
The influence of high compaction pressure on cordierite-based ceramics
(Bor : University of Belgrade, Technical Faculty in Bor, 2021)
Cordierite, 2MgO⋅2Al2O3⋅5SiO2 is a high-temperature ceramic material. In order to improve its properties, titanium oxide was added to the starting mixture in an amount of 5%. Mechanical activation of samples was performed ...
SEM and X-ray analyses of sintered MgO/Bi2O3 binary system
(Bor : University of Belgrade, Technical Faculty in Bor, 2021)
Cordierite, 2MgO⋅2Al2O3⋅5SiO2 is a high-temperature ceramic material. In order to improve its properties, titanium oxide was added to the starting mixture in an amount of 5%. Mechanical activation of samples was performed ...