Mixtures of BaCO3-ZnO-TiO2 were mechanically activated using high-energy planetary ball mill during 20, 40 and 80 min. As the time of mechanical activation increased, the decrease in particle size was observed. The effect of milling on microstructure was investigated by scanning electron microscopy, as well. Sintering process was performed in air at 1100 and 1200 C for 2 h. Various phases are present within mixtures sintered at 1100 and 1200 degrees C, and almost pure BaZn2Ti4O11 phase was obtained after 80 min of milling and sintering at 1200 degrees C for 2 h.
Кључне речи:
X-ray methods / Traditional ceramics / Sintering / Milling
TY - JOUR
AU - Obradović, Nina
AU - Filipović, Suzana
AU - Pavlović, V.
AU - Mitrić, Miodrag
AU - Marković, Smilja
AU - Mitić, Vojislav V.
AU - Đorđević, Nataša
AU - Ristić, M. M.
PY - 2011
UR - https://ritnms.itnms.ac.rs/handle/123456789/201
AB - Mixtures of BaCO3-ZnO-TiO2 were mechanically activated using high-energy planetary ball mill during 20, 40 and 80 min. As the time of mechanical activation increased, the decrease in particle size was observed. The effect of milling on microstructure was investigated by scanning electron microscopy, as well. Sintering process was performed in air at 1100 and 1200 C for 2 h. Various phases are present within mixtures sintered at 1100 and 1200 degrees C, and almost pure BaZn2Ti4O11 phase was obtained after 80 min of milling and sintering at 1200 degrees C for 2 h.
PB - Elsevier Sci Ltd, Oxford
T2 - Ceramics International
T1 - Isothermal sintering of barium-zinc-titanate ceramics
EP - 27
IS - 1
SP - 21
VL - 37
DO - 10.1016/j.ceramint.2010.07.001
UR - conv_596
ER -
@article{
author = "Obradović, Nina and Filipović, Suzana and Pavlović, V. and Mitrić, Miodrag and Marković, Smilja and Mitić, Vojislav V. and Đorđević, Nataša and Ristić, M. M.",
year = "2011",
abstract = "Mixtures of BaCO3-ZnO-TiO2 were mechanically activated using high-energy planetary ball mill during 20, 40 and 80 min. As the time of mechanical activation increased, the decrease in particle size was observed. The effect of milling on microstructure was investigated by scanning electron microscopy, as well. Sintering process was performed in air at 1100 and 1200 C for 2 h. Various phases are present within mixtures sintered at 1100 and 1200 degrees C, and almost pure BaZn2Ti4O11 phase was obtained after 80 min of milling and sintering at 1200 degrees C for 2 h.",
publisher = "Elsevier Sci Ltd, Oxford",
journal = "Ceramics International",
title = "Isothermal sintering of barium-zinc-titanate ceramics",
pages = "27-21",
number = "1",
volume = "37",
doi = "10.1016/j.ceramint.2010.07.001",
url = "conv_596"
}
Obradović, N., Filipović, S., Pavlović, V., Mitrić, M., Marković, S., Mitić, V. V., Đorđević, N.,& Ristić, M. M.. (2011). Isothermal sintering of barium-zinc-titanate ceramics. in Ceramics International
Elsevier Sci Ltd, Oxford., 37(1), 21-27.
https://doi.org/10.1016/j.ceramint.2010.07.001
conv_596
Obradović N, Filipović S, Pavlović V, Mitrić M, Marković S, Mitić VV, Đorđević N, Ristić MM. Isothermal sintering of barium-zinc-titanate ceramics. in Ceramics International. 2011;37(1):21-27.
doi:10.1016/j.ceramint.2010.07.001
conv_596 .
Obradović, Nina, Filipović, Suzana, Pavlović, V., Mitrić, Miodrag, Marković, Smilja, Mitić, Vojislav V., Đorđević, Nataša, Ristić, M. M., "Isothermal sintering of barium-zinc-titanate ceramics" in Ceramics International, 37, no. 1 (2011):21-27,
https://doi.org/10.1016/j.ceramint.2010.07.001 .,
conv_596 .