High strength low-alloyed (HSLA) Cr-Mn-Si steels belong to a group of steels that can reach their full mechanical properties after quenching and tempering. Those properties depend both on the temperature and time of tempering. Knowing the tempering parameters, it is possible to reach the desired properties of the treated steel. Some results on investigating the Hollomon-Jaffe equation (in parametric form) application for tempering of HSLA steel, are shown in this paper. The experiments were performed in real production conditions, using a standard material. The quenching was performed at 870°C, the heating period was always 30 min, with subsequent cooling into the oil bath. The tempering was carried out in temperature range from 480 to 680°C, while tempering time varied from 15 min to 24 h. The degree of tempering is referred through the hardness values changing. The experimental results have shown a pretty well agreement to tempering parameters, included in Hollomon-Jaffe equation, fo...r this kind of HSLA steel.
TY - JOUR
AU - Janjušević, Zoran
AU - Gulišija, Zvonko
AU - Mihailović, Marija
AU - Patarić, Aleksandra
PY - 2009
UR - https://ritnms.itnms.ac.rs/handle/123456789/146
AB - High strength low-alloyed (HSLA) Cr-Mn-Si steels belong to a group of steels that can reach their full mechanical properties after quenching and tempering. Those properties depend both on the temperature and time of tempering. Knowing the tempering parameters, it is possible to reach the desired properties of the treated steel. Some results on investigating the Hollomon-Jaffe equation (in parametric form) application for tempering of HSLA steel, are shown in this paper. The experiments were performed in real production conditions, using a standard material. The quenching was performed at 870°C, the heating period was always 30 min, with subsequent cooling into the oil bath. The tempering was carried out in temperature range from 480 to 680°C, while tempering time varied from 15 min to 24 h. The degree of tempering is referred through the hardness values changing. The experimental results have shown a pretty well agreement to tempering parameters, included in Hollomon-Jaffe equation, for this kind of HSLA steel.
PB - Savez hemijskih inženjera, Beograd
T2 - Chemical Industry and Chemical Engineering Quarterly / CICEQ
T1 - The investigation of applicability of the Hollomon-Jaffe equation on tempering the HSLA steel
EP - 136
IS - 3
SP - 131
VL - 15
DO - 10.2298/CICEQ0903131J
UR - conv_386
ER -
@article{
author = "Janjušević, Zoran and Gulišija, Zvonko and Mihailović, Marija and Patarić, Aleksandra",
year = "2009",
abstract = "High strength low-alloyed (HSLA) Cr-Mn-Si steels belong to a group of steels that can reach their full mechanical properties after quenching and tempering. Those properties depend both on the temperature and time of tempering. Knowing the tempering parameters, it is possible to reach the desired properties of the treated steel. Some results on investigating the Hollomon-Jaffe equation (in parametric form) application for tempering of HSLA steel, are shown in this paper. The experiments were performed in real production conditions, using a standard material. The quenching was performed at 870°C, the heating period was always 30 min, with subsequent cooling into the oil bath. The tempering was carried out in temperature range from 480 to 680°C, while tempering time varied from 15 min to 24 h. The degree of tempering is referred through the hardness values changing. The experimental results have shown a pretty well agreement to tempering parameters, included in Hollomon-Jaffe equation, for this kind of HSLA steel.",
publisher = "Savez hemijskih inženjera, Beograd",
journal = "Chemical Industry and Chemical Engineering Quarterly / CICEQ",
title = "The investigation of applicability of the Hollomon-Jaffe equation on tempering the HSLA steel",
pages = "136-131",
number = "3",
volume = "15",
doi = "10.2298/CICEQ0903131J",
url = "conv_386"
}
Janjušević, Z., Gulišija, Z., Mihailović, M.,& Patarić, A.. (2009). The investigation of applicability of the Hollomon-Jaffe equation on tempering the HSLA steel. in Chemical Industry and Chemical Engineering Quarterly / CICEQ
Savez hemijskih inženjera, Beograd., 15(3), 131-136.
https://doi.org/10.2298/CICEQ0903131J
conv_386
Janjušević Z, Gulišija Z, Mihailović M, Patarić A. The investigation of applicability of the Hollomon-Jaffe equation on tempering the HSLA steel. in Chemical Industry and Chemical Engineering Quarterly / CICEQ. 2009;15(3):131-136.
doi:10.2298/CICEQ0903131J
conv_386 .
Janjušević, Zoran, Gulišija, Zvonko, Mihailović, Marija, Patarić, Aleksandra, "The investigation of applicability of the Hollomon-Jaffe equation on tempering the HSLA steel" in Chemical Industry and Chemical Engineering Quarterly / CICEQ, 15, no. 3 (2009):131-136,
https://doi.org/10.2298/CICEQ0903131J .,
conv_386 .