Design of microstructure of ceramics based on waste fly ash and clay

Jovanov, Vojo; Anguseva, Biljana; Pantović, Katarina; Fidancevska, Emilija

(Bor : University of Belgrade, Technical Faculty in Bor, 2015) 

TY  - CONF
AU  - Jovanov, Vojo
AU  - Anguseva, Biljana
AU  - Pantović, Katarina
AU  - Fidancevska, Emilija
PY  - 2015
UR  - https://ritnms.itnms.ac.rs/handle/123456789/1117
AB  - Ceramics microstructure was designed using waste flay ash (REK Bitola, Macedonia) and clay. The raw materials were characterized from chemical, mineralogical and thermal aspect. The ceramics was designed using the granulation less than 0.063 mm. The clay content varied from 10 to 90 wt.%. The consolidation of the compacts was realized at pressure of 45 MPa and sintering at different temperatures (900, 1000, 1500 and 1100 oC/1h, heating rate of 10oC/min).  
The designed microstructure of the composite with composition 60wt% clay and 40wt% fly ash sintered at 1100oC/1h was found as optimal regarding to its properties: density- 2.089g/cm2;  water absorption- 7.02%, bending strength – 50.47 MPa and E-modulus - 25,35GPa. Technical coefficient of thermal expansion was α20-600=7.03x10-6/oC.
PB  - Bor : University of Belgrade, Technical Faculty in Bor
C3  - XXIII International Conference  "ECOLOGICAL TRUTH" Eco-Ist'15
T1  - Design of microstructure of ceramics based on waste fly ash and clay
EP  - 211
SP  - 207
ER  - 
@conference{
author = "Jovanov, Vojo and Anguseva, Biljana and Pantović, Katarina and Fidancevska, Emilija",
year = "2015",
abstract = "Ceramics microstructure was designed using waste flay ash (REK Bitola, Macedonia) and clay. The raw materials were characterized from chemical, mineralogical and thermal aspect. The ceramics was designed using the granulation less than 0.063 mm. The clay content varied from 10 to 90 wt.%. The consolidation of the compacts was realized at pressure of 45 MPa and sintering at different temperatures (900, 1000, 1500 and 1100 oC/1h, heating rate of 10oC/min).  
The designed microstructure of the composite with composition 60wt% clay and 40wt% fly ash sintered at 1100oC/1h was found as optimal regarding to its properties: density- 2.089g/cm2;  water absorption- 7.02%, bending strength – 50.47 MPa and E-modulus - 25,35GPa. Technical coefficient of thermal expansion was α20-600=7.03x10-6/oC.",
publisher = "Bor : University of Belgrade, Technical Faculty in Bor",
journal = "XXIII International Conference  "ECOLOGICAL TRUTH" Eco-Ist'15",
title = "Design of microstructure of ceramics based on waste fly ash and clay",
pages = "211-207"
}
Jovanov, V., Anguseva, B., Pantović, K.,& Fidancevska, E.. (2015). Design of microstructure of ceramics based on waste fly ash and clay. in XXIII International Conference  "ECOLOGICAL TRUTH" Eco-Ist'15
Bor : University of Belgrade, Technical Faculty in Bor., 207-211.
Jovanov V, Anguseva B, Pantović K, Fidancevska E. Design of microstructure of ceramics based on waste fly ash and clay. in XXIII International Conference  "ECOLOGICAL TRUTH" Eco-Ist'15. 2015;:207-211..
Jovanov, Vojo, Anguseva, Biljana, Pantović, Katarina, Fidancevska, Emilija, "Design of microstructure of ceramics based on waste fly ash and clay" in XXIII International Conference  "ECOLOGICAL TRUTH" Eco-Ist'15 (2015):207-211.