@conference{
author = "Đorđević, Nataša and Mihajlović, Slavica and Obradović, Nina and Peleš, Adrijana and Filipović, Suzana",
year = "2021",
abstract = "Cordierite, 2MgO⋅2Al2O3⋅5SiO2 is a high-temperature ceramic material. In order to improve its properties, titanium oxide was added to the starting mixture in an amount of 5%. Mechanical activation of samples was performed in a high-energy ball mill for 10 minutes. The compaction pressure was unusually high, 6 t cm-2 (588 MPa) in order to compare to previous research. Cordierite was sintered at the temperature of 1375°C. The phase composition of the activated and sintered samples was analyzed using X-ray diffraction. Scanning electron microscopy was used to analyze the microstructure of both compacted and sintered samples.",
publisher = "Bor : University of Belgrade, Technical Faculty in Bor",
journal = "52nd International October Conference on Mining and Metallurgy, (IOC 2021)",
title = "The influence of high compaction pressure on cordierite-based ceramics",
pages = "148-145"
}