Synthesis of alpha-al2o3 based foams with improved properties as catalyst carriers
Апстракт
This paper explores the possibility of synthesising catalyst supports with improved properties. Alumina foams were produced with the polymer replication technique. Representative high- and low-temperature sintering ceramics were selected. Suitable suspension amounts, the clay addition and sintering temperature were determined. A lower sintering temperature was used for an economic enhancement of the process. The sintering was conducted at the temperatures from 1573 K to 1773 K for 60 min. A comparative analysis of the studied systems shows that the best compressive strength of 6.2 MPa was achieved with the system based on the alpha-Al2O3-25 clay (mass fractions, w/%), polyester foam with 10 PPI, sintered at 1673 K.
Кључне речи:
sintering / reticulated foam / mechanical properties / catalyst carrier / aluminaИзвор:
Materiali in Tehnologije, 2014, 48, 1, 45-50Издавач:
- Institute of Metals and Technology
Финансирање / пројекти:
- Иновативна синергија нус-продуката, минимизације отпада и чистије производње у металургији (RS-MESTD-Technological Development (TD or TR)-34033)
- Развој технолошких процеса прераде нестандардних концентрата бакра у циљу оптимизације емисије загађујућих материја (RS-MESTD-Technological Development (TD or TR)-34023)
Институција/група
Institut za tehnologiju nuklearnih i drugih mineralnih sirovinaTY - JOUR AU - Nikolić, Vesna AU - Kamberović, Željko AU - Andić, Zoran AU - Korać, Marija AU - Sokić, Miroslav PY - 2014 UR - https://ritnms.itnms.ac.rs/handle/123456789/292 AB - This paper explores the possibility of synthesising catalyst supports with improved properties. Alumina foams were produced with the polymer replication technique. Representative high- and low-temperature sintering ceramics were selected. Suitable suspension amounts, the clay addition and sintering temperature were determined. A lower sintering temperature was used for an economic enhancement of the process. The sintering was conducted at the temperatures from 1573 K to 1773 K for 60 min. A comparative analysis of the studied systems shows that the best compressive strength of 6.2 MPa was achieved with the system based on the alpha-Al2O3-25 clay (mass fractions, w/%), polyester foam with 10 PPI, sintered at 1673 K. PB - Institute of Metals and Technology T2 - Materiali in Tehnologije T1 - Synthesis of alpha-al2o3 based foams with improved properties as catalyst carriers EP - 50 IS - 1 SP - 45 VL - 48 UR - https://hdl.handle.net/21.15107/rcub_technorep_2562 UR - conv_1042 ER -
@article{ author = "Nikolić, Vesna and Kamberović, Željko and Andić, Zoran and Korać, Marija and Sokić, Miroslav", year = "2014", abstract = "This paper explores the possibility of synthesising catalyst supports with improved properties. Alumina foams were produced with the polymer replication technique. Representative high- and low-temperature sintering ceramics were selected. Suitable suspension amounts, the clay addition and sintering temperature were determined. A lower sintering temperature was used for an economic enhancement of the process. The sintering was conducted at the temperatures from 1573 K to 1773 K for 60 min. A comparative analysis of the studied systems shows that the best compressive strength of 6.2 MPa was achieved with the system based on the alpha-Al2O3-25 clay (mass fractions, w/%), polyester foam with 10 PPI, sintered at 1673 K.", publisher = "Institute of Metals and Technology", journal = "Materiali in Tehnologije", title = "Synthesis of alpha-al2o3 based foams with improved properties as catalyst carriers", pages = "50-45", number = "1", volume = "48", url = "https://hdl.handle.net/21.15107/rcub_technorep_2562, conv_1042" }
Nikolić, V., Kamberović, Ž., Andić, Z., Korać, M.,& Sokić, M.. (2014). Synthesis of alpha-al2o3 based foams with improved properties as catalyst carriers. in Materiali in Tehnologije Institute of Metals and Technology., 48(1), 45-50. https://hdl.handle.net/21.15107/rcub_technorep_2562
Nikolić V, Kamberović Ž, Andić Z, Korać M, Sokić M. Synthesis of alpha-al2o3 based foams with improved properties as catalyst carriers. in Materiali in Tehnologije. 2014;48(1):45-50. https://hdl.handle.net/21.15107/rcub_technorep_2562 .
Nikolić, Vesna, Kamberović, Željko, Andić, Zoran, Korać, Marija, Sokić, Miroslav, "Synthesis of alpha-al2o3 based foams with improved properties as catalyst carriers" in Materiali in Tehnologije, 48, no. 1 (2014):45-50, https://hdl.handle.net/21.15107/rcub_technorep_2562 .