Uticaj mehaničke energije na komponente MgO-Al2O3-SiO2-TiO2 sistema
Influence of mechanical activation on the constituents of the MgO-Al2O3-SiO2-TiO2 system
Nema prikaza
Autori
Đorđević, Nataša![](/themes/Mirageritnms/images/orcid.png)
Obradović, Nina
![](/themes/Mirageritnms/images/orcid.png)
Filipović, Suzana
![](/themes/Mirageritnms/images/orcid.png)
Živojinović, Jelena
![](/themes/Mirageritnms/images/orcid.png)
Mitrić, Miodrag
![](/themes/Mirageritnms/images/orcid.png)
Marković, Smilja
![](/themes/Mirageritnms/images/orcid.png)
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
U ovom radu je ispitivan uticaj mehaničke energije na strukturu i promene u mikrostrukturi sistema MgO-Al2O3-SiO2-TiO2. Utvrđeno je da mehanička energija pospešuje homogenizaciju polaznih komponenti, utiče na veličinu i oblik zrna praškastih materijala i podstiče promene u kristalnoj strukturi polaznih čestica, sto utiče na pojavu defekata u ispitivanom sistemu. Ove promene su utvrđene difraktometrijskom analizom, kao i PSA i DTA metodom.
In this paper the effects of mechanical activation on structural and microstructural changes of the system MgO-Al2O3-SiO2-TiO2 were analyzed. It was confirmed that mechanical activation led to the homogenization of powder particles, the comminuting of particles, and after this period, the introduced energy was used to induce changes in the crystal structure, which resulted in the emergence of defects, initially on the surface of the crystal lattice, and then inside.
Ključne reči:
mehanicka aktivacija / kordijerit TiO2 / TiO2 / mechanical activation / cordieriteIzvor:
Tehnika, 2012, 67, 3, 329-333Izdavač:
- Savez inženjera i tehničara Srbije, Beograd
Finansiranje / projekti:
- Usmerena sinteza, struktura i svojstva multifunkcionalnih materijala (RS-MESTD-Basic Research (BR or ON)-172057)
Institucija/grupa
Institut za tehnologiju nuklearnih i drugih mineralnih sirovinaTY - JOUR AU - Đorđević, Nataša AU - Obradović, Nina AU - Filipović, Suzana AU - Živojinović, Jelena AU - Mitrić, Miodrag AU - Marković, Smilja PY - 2012 UR - https://ritnms.itnms.ac.rs/handle/123456789/239 AB - U ovom radu je ispitivan uticaj mehaničke energije na strukturu i promene u mikrostrukturi sistema MgO-Al2O3-SiO2-TiO2. Utvrđeno je da mehanička energija pospešuje homogenizaciju polaznih komponenti, utiče na veličinu i oblik zrna praškastih materijala i podstiče promene u kristalnoj strukturi polaznih čestica, sto utiče na pojavu defekata u ispitivanom sistemu. Ove promene su utvrđene difraktometrijskom analizom, kao i PSA i DTA metodom. AB - In this paper the effects of mechanical activation on structural and microstructural changes of the system MgO-Al2O3-SiO2-TiO2 were analyzed. It was confirmed that mechanical activation led to the homogenization of powder particles, the comminuting of particles, and after this period, the introduced energy was used to induce changes in the crystal structure, which resulted in the emergence of defects, initially on the surface of the crystal lattice, and then inside. PB - Savez inženjera i tehničara Srbije, Beograd T2 - Tehnika T1 - Uticaj mehaničke energije na komponente MgO-Al2O3-SiO2-TiO2 sistema T1 - Influence of mechanical activation on the constituents of the MgO-Al2O3-SiO2-TiO2 system EP - 333 IS - 3 SP - 329 VL - 67 UR - conv_7 ER -
@article{ author = "Đorđević, Nataša and Obradović, Nina and Filipović, Suzana and Živojinović, Jelena and Mitrić, Miodrag and Marković, Smilja", year = "2012", abstract = "U ovom radu je ispitivan uticaj mehaničke energije na strukturu i promene u mikrostrukturi sistema MgO-Al2O3-SiO2-TiO2. Utvrđeno je da mehanička energija pospešuje homogenizaciju polaznih komponenti, utiče na veličinu i oblik zrna praškastih materijala i podstiče promene u kristalnoj strukturi polaznih čestica, sto utiče na pojavu defekata u ispitivanom sistemu. Ove promene su utvrđene difraktometrijskom analizom, kao i PSA i DTA metodom., In this paper the effects of mechanical activation on structural and microstructural changes of the system MgO-Al2O3-SiO2-TiO2 were analyzed. It was confirmed that mechanical activation led to the homogenization of powder particles, the comminuting of particles, and after this period, the introduced energy was used to induce changes in the crystal structure, which resulted in the emergence of defects, initially on the surface of the crystal lattice, and then inside.", publisher = "Savez inženjera i tehničara Srbije, Beograd", journal = "Tehnika", title = "Uticaj mehaničke energije na komponente MgO-Al2O3-SiO2-TiO2 sistema, Influence of mechanical activation on the constituents of the MgO-Al2O3-SiO2-TiO2 system", pages = "333-329", number = "3", volume = "67", url = "conv_7" }
Đorđević, N., Obradović, N., Filipović, S., Živojinović, J., Mitrić, M.,& Marković, S.. (2012). Uticaj mehaničke energije na komponente MgO-Al2O3-SiO2-TiO2 sistema. in Tehnika Savez inženjera i tehničara Srbije, Beograd., 67(3), 329-333. conv_7
Đorđević N, Obradović N, Filipović S, Živojinović J, Mitrić M, Marković S. Uticaj mehaničke energije na komponente MgO-Al2O3-SiO2-TiO2 sistema. in Tehnika. 2012;67(3):329-333. conv_7 .
Đorđević, Nataša, Obradović, Nina, Filipović, Suzana, Živojinović, Jelena, Mitrić, Miodrag, Marković, Smilja, "Uticaj mehaničke energije na komponente MgO-Al2O3-SiO2-TiO2 sistema" in Tehnika, 67, no. 3 (2012):329-333, conv_7 .