Chemical durability of sintered glass-composite prepared from glass cullet and waste foundry sand
2021
Аутори
Savić, VeljkoTopalović, Vladimir
Matijašević, Srđan
Nikolić, Jelena
Grujić, Snežana
Zildžović, Snežana
Radulović, Aleksandra
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
In this study, the glass-composite was prepared using glass cullet and waste foundry sand as raw materials. The powder technology route was employed. The mixtures containing 10-50 wt% of the sand were sintered at T = 750 degrees C for t =1h. XRD and DTA analyses were performed. The chemical durability of the resulting glass-composite was determined by leaching test in HCl, H2SO4, NaOH and distilled water at T = 95 degrees C for t =1h. It was shown that the sintering process carried out without the crystallization of the glass matrix. The lowest chemical durability was determined in alkali solution of glasscomposite.
Кључне речи:
waste foundry sand / sintering / glass-composite / glass culletИзвор:
Metallurgical & Materials Engineering, 2021, 27, 1, 105-113Издавач:
- Savez inženjera metalurgije Srbije, Beograd
Финансирање / пројекти:
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200023 (Институт за технологију нуклеарних и других минералних сировина - ИТНМС, Београд) (RS-MESTD-inst-2020-200023)
DOI: 10.30544/477
ISSN: 2217-8961
WoS: 000636434600008
Scopus: 2-s2.0-85104000253
Институција/група
Institut za tehnologiju nuklearnih i drugih mineralnih sirovinaTY - JOUR AU - Savić, Veljko AU - Topalović, Vladimir AU - Matijašević, Srđan AU - Nikolić, Jelena AU - Grujić, Snežana AU - Zildžović, Snežana AU - Radulović, Aleksandra PY - 2021 UR - https://ritnms.itnms.ac.rs/handle/123456789/597 AB - In this study, the glass-composite was prepared using glass cullet and waste foundry sand as raw materials. The powder technology route was employed. The mixtures containing 10-50 wt% of the sand were sintered at T = 750 degrees C for t =1h. XRD and DTA analyses were performed. The chemical durability of the resulting glass-composite was determined by leaching test in HCl, H2SO4, NaOH and distilled water at T = 95 degrees C for t =1h. It was shown that the sintering process carried out without the crystallization of the glass matrix. The lowest chemical durability was determined in alkali solution of glasscomposite. PB - Savez inženjera metalurgije Srbije, Beograd T2 - Metallurgical & Materials Engineering T1 - Chemical durability of sintered glass-composite prepared from glass cullet and waste foundry sand EP - 113 IS - 1 SP - 105 VL - 27 DO - 10.30544/477 UR - conv_906 ER -
@article{ author = "Savić, Veljko and Topalović, Vladimir and Matijašević, Srđan and Nikolić, Jelena and Grujić, Snežana and Zildžović, Snežana and Radulović, Aleksandra", year = "2021", abstract = "In this study, the glass-composite was prepared using glass cullet and waste foundry sand as raw materials. The powder technology route was employed. The mixtures containing 10-50 wt% of the sand were sintered at T = 750 degrees C for t =1h. XRD and DTA analyses were performed. The chemical durability of the resulting glass-composite was determined by leaching test in HCl, H2SO4, NaOH and distilled water at T = 95 degrees C for t =1h. It was shown that the sintering process carried out without the crystallization of the glass matrix. The lowest chemical durability was determined in alkali solution of glasscomposite.", publisher = "Savez inženjera metalurgije Srbije, Beograd", journal = "Metallurgical & Materials Engineering", title = "Chemical durability of sintered glass-composite prepared from glass cullet and waste foundry sand", pages = "113-105", number = "1", volume = "27", doi = "10.30544/477", url = "conv_906" }
Savić, V., Topalović, V., Matijašević, S., Nikolić, J., Grujić, S., Zildžović, S.,& Radulović, A.. (2021). Chemical durability of sintered glass-composite prepared from glass cullet and waste foundry sand. in Metallurgical & Materials Engineering Savez inženjera metalurgije Srbije, Beograd., 27(1), 105-113. https://doi.org/10.30544/477 conv_906
Savić V, Topalović V, Matijašević S, Nikolić J, Grujić S, Zildžović S, Radulović A. Chemical durability of sintered glass-composite prepared from glass cullet and waste foundry sand. in Metallurgical & Materials Engineering. 2021;27(1):105-113. doi:10.30544/477 conv_906 .
Savić, Veljko, Topalović, Vladimir, Matijašević, Srđan, Nikolić, Jelena, Grujić, Snežana, Zildžović, Snežana, Radulović, Aleksandra, "Chemical durability of sintered glass-composite prepared from glass cullet and waste foundry sand" in Metallurgical & Materials Engineering, 27, no. 1 (2021):105-113, https://doi.org/10.30544/477 ., conv_906 .