SEM and X-ray analyses of sintered MgO/Bi2O3 binary system
2021
Аутори
Đorđević, NatašaMihajlović, Slavica
Sokić, Miroslav
Marković, Branislav
Остала ауторства
Stojadinović, SašaPetrović, Dejan
Конференцијски прилог (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Cordierite, 2MgO⋅2Al2O3⋅5SiO2 is a high-temperature ceramic material. In order to improve its properties, titanium oxide was added to the starting mixture in an amount of 5%. Mechanical activation of samples was performed in a high-energy ball mill for 10 minutes. The compaction pressure was unusually high, 6 t cm-2 (588 MPa) in order to compare to previous research. Cordierite was sintered at the temperature of 1375°C. The phase composition of the activated and sintered samples was analyzed using X-ray diffraction. Scanning electron microscopy was used to analyze the microstructure of both compacted and sintered samples.
Кључне речи:
mechanical activation / cordierite / XRD / SEMИзвор:
52nd International October Conference on Mining and Metallurgy, (IOC 2021), 2021, 149-152Издавач:
- Bor : University of Belgrade, Technical Faculty in Bor
Финансирање / пројекти:
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200023 (Институт за технологију нуклеарних и других минералних сировина - ИТНМС, Београд) (RS-MESTD-inst-2020-200023)
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200026 (Универзитет у Београду, Институт за хемију, технологију и металургију - ИХТМ) (RS-MESTD-inst-2020-200026)
Институција/група
Institut za tehnologiju nuklearnih i drugih mineralnih sirovinaTY - CONF AU - Đorđević, Nataša AU - Mihajlović, Slavica AU - Sokić, Miroslav AU - Marković, Branislav PY - 2021 UR - https://ritnms.itnms.ac.rs/handle/123456789/1132 AB - Cordierite, 2MgO⋅2Al2O3⋅5SiO2 is a high-temperature ceramic material. In order to improve its properties, titanium oxide was added to the starting mixture in an amount of 5%. Mechanical activation of samples was performed in a high-energy ball mill for 10 minutes. The compaction pressure was unusually high, 6 t cm-2 (588 MPa) in order to compare to previous research. Cordierite was sintered at the temperature of 1375°C. The phase composition of the activated and sintered samples was analyzed using X-ray diffraction. Scanning electron microscopy was used to analyze the microstructure of both compacted and sintered samples. PB - Bor : University of Belgrade, Technical Faculty in Bor C3 - 52nd International October Conference on Mining and Metallurgy, (IOC 2021) T1 - SEM and X-ray analyses of sintered MgO/Bi2O3 binary system EP - 152 SP - 149 ER -
@conference{ author = "Đorđević, Nataša and Mihajlović, Slavica and Sokić, Miroslav and Marković, Branislav", year = "2021", abstract = "Cordierite, 2MgO⋅2Al2O3⋅5SiO2 is a high-temperature ceramic material. In order to improve its properties, titanium oxide was added to the starting mixture in an amount of 5%. Mechanical activation of samples was performed in a high-energy ball mill for 10 minutes. The compaction pressure was unusually high, 6 t cm-2 (588 MPa) in order to compare to previous research. Cordierite was sintered at the temperature of 1375°C. The phase composition of the activated and sintered samples was analyzed using X-ray diffraction. Scanning electron microscopy was used to analyze the microstructure of both compacted and sintered samples.", publisher = "Bor : University of Belgrade, Technical Faculty in Bor", journal = "52nd International October Conference on Mining and Metallurgy, (IOC 2021)", title = "SEM and X-ray analyses of sintered MgO/Bi2O3 binary system", pages = "152-149" }
Đorđević, N., Mihajlović, S., Sokić, M.,& Marković, B.. (2021). SEM and X-ray analyses of sintered MgO/Bi2O3 binary system. in 52nd International October Conference on Mining and Metallurgy, (IOC 2021) Bor : University of Belgrade, Technical Faculty in Bor., 149-152.
Đorđević N, Mihajlović S, Sokić M, Marković B. SEM and X-ray analyses of sintered MgO/Bi2O3 binary system. in 52nd International October Conference on Mining and Metallurgy, (IOC 2021). 2021;:149-152..
Đorđević, Nataša, Mihajlović, Slavica, Sokić, Miroslav, Marković, Branislav, "SEM and X-ray analyses of sintered MgO/Bi2O3 binary system" in 52nd International October Conference on Mining and Metallurgy, (IOC 2021) (2021):149-152.